"shock absorber piston"

Alloy powder good tolerance shock base valve density 6.6 g/cm3 without steam treatment Specifications: Density 6.2-6.8 g/cm3 Hardness HRB 45-65 Steam treatment 2H high temp steam holding time Thickness of Fe3O4 0.004-0.005mm Description: HRB45-65 Iron-Copper and Copper Steel Sintered Parts for car shock absorbers Our company produces different kinds of sintered parts. These sintered part include pistons, foot valve, rod guider, valve base and so on. Dimension: D32.5XD6X11.5

PTFE bands with various filler assembled on OD of sinter piston Specifications: properties unit result Apparent density g/cm3 2.10-2.30 Tensile strength(min) MPa 15.0 Ultimate elongation(min) % 150 Working Temp. ℃ -180~260 Melting point ℃ 327 Produce Max Temp. ℃ 385 Size mm 20mm~400mm 1. Good sealing effect in Dynamic and static sealing 2. Minimal start-up and movement friction, smooth movement even at low speeds, no creeping phenomenon. 3. Good abrasion. Description: Carbon

Black Density 2.16g / cm3 PTFE Bands with various filler assembled on piston outside Specifications: properties unit result Apparent density g/cm3 2.10-2.30 Tensile strength(min) MPa 15.0 Ultimate elongation(min) % 150 Working Temp. ℃ -180~260 Melting point ℃ 327 Produce Max Temp. ℃ 385 Size mm 20mm~400mm 1. Good sealing effect in Dynamic and static sealing 2. Minimal start-up and movement friction, smooth movement even at low speeds, no creeping phenomenon. 3. Good

Popular Heavy Duty Shock Base Valve with Rust Preventive Export to Europe Market Manufacturability 1.Auto Mechanical Press:50T, 100T, 140T 2.Hydraulic Press:100T, 315T, 600T, 800T 3.Six sinter furnaces, including one harden Sinter Furnace 4.In-house tooling making:EDM, wire cutting machine Specifications: Density 6.2-6.8 g/cm3 Hardness HRB 45-65 Steam treatment 2H high temp steam holding time Thickness of Fe3O4 0.004-0.005mm Description: HRB80-100 Iron-Copper and Copper Steel

Base Valve Foot Valve Powdered Metal Parts With Steam Treatment Applied in Car Shocks Manufacturability 1. Auto Mechanical Press:50T, 100T, 140T 2. Hydraulic Press:100T, 315T, 600T, 800T 3. Six sinter furnaces, including one harden Sinter Furnace 4. In-house tooling making:EDM, wire cutting machine Specifications: Density 6.2-6.8 g/cm3 Hardness HRB 45-65 Steam treatment 2H high temp steam holding time Thickness of Fe3O4 0.004-0.005mm Description: HRB80-100 Iron-Copper and

45mm For Heavy Duty Truck Density 6.65 g/cm3 Shock Base Valve Foot Valve​ with Rust Preventive Export to Europe Market Manufacturability 1.Auto Mechanical Press:50T, 100T, 140T 2.Hydraulic Press:100T, 315T, 600T, 800T 3.Six sinter furnaces, including one harden Sinter Furnace 4.In-house tooling making:EDM, wire cutting machine Specifications: Density 6.2-6.8 g/cm3 Hardness HRB 45-65 Steam treatment 2H high temp steam holding time Thickness of Fe3O4 0.004-0.005mm Description:

high temp resist PTFE ring gasket with density 2.15 used to band PTFE on pistons Specifications: properties unit result Apparent density g/cm3 2.10-2.30 Tensile strength(min) MPa 15.0 Ultimate elongation(min) % 150 Working Temp. ℃ -180~260 Melting point ℃ 327 Produce Max Temp. ℃ 385 Size mm 20mm~400mm 1. Good sealing effect in Dynamic and static sealing 2. Minimal start-up and movement friction, smooth movement even at low speeds, no creeping phenomenon. 3. Good abrasion. 4

High Tensile Strength Green PTFE Ring Gasket With Copper Filler For Pistons Banding Specifications: properties unit result Apparent density g/cm3 2.10-2.30 Tensile strength(min) MPa 15.0 Ultimate elongation(min) % 150 Working Temp. ℃ -180~260 Melting point ℃ 327 Produce Max Temp. ℃ 385 Size mm 20mm~400mm Products Name: From your specification Custom PTFE ring Material Comparison: PTFE, Filler PTFE Application: Industry, Chemistry and so on Design: By Customer Processing

Low Friction Coefficient Oil Guide Ring Assembled In Shock Rod Guide With Good Seals Oil guide ring with different types and size in our stock. Produced by automatic pressing machine and heated more than 10 hours with 16 different temperature. Sintering curve is controlled by computer. parts are 100% checked by GO & NO-GO gauge. We can produce according to customer's drawings. It will take about one week for new toolings. Specifications: Item unit value Density g/cm3 2.18